SCIENCE CHINA Materials, Volume 62 , Issue 12 : 1898-1909(2019) https://doi.org/10.1007/s40843-019-9469-4

Dense and pure high-entropy metal diboride ceramics sintered from self-synthesized powders via boro/carbothermal reduction approach

More info
  • ReceivedApr 9, 2019
  • AcceptedJul 1, 2019
  • PublishedJul 31, 2019


Funded by

the National Natural Science Foundation of China(51521001,51832003)

and the Fundamental Research Funds for the Central Universities.


This work was financially supported by the National Natural Science Foundation of China (51521001 and 51832003), and the Fundamental Research Funds for the Central Universities.

Interest statement

These authors declare no conflict of interest.

Contributions statement

Zou J and Fu ZY designed the research. Gu J and Zou J performed the experiments with the help of Wang H, Wang W, Zhang J and Fu ZY. Sun SK performed the XRD refinement. Yu SY and Zou J performed the hardness test. Fu Z supervised and acquired funding for the research. Gu J and Zou J wrote the paper. All authors discussed the results and commented on the manuscript.

Author information

Junfeng Gu is currently a PhD student at the State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology. His research focuses on the sintering mechanisms and properties of ultra-high temperature ceramics.

Ji Zou is a Research Fellow at the University of Birmingham, UK and an adjunct professor at Wuhan Institute of Technology, China. He received his PhD degree from Shanghai Institute of Ceramics, Chinese Academy of Sciences. He has been active in the processing-structure-property correlation of ceramics, especially for boride ceramics.

Zhengyi Fu is a chief professor at the State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology. He received his PhD degree from Wuhan University of Technology in 1994. His current research interests include advanced sintering and bioprocess-inspired fabrication.


Supplementary information

Supporting data are available in the online version of this paper.


[1] Yeh JW, Chen SK, Lin SJ, et al. Nanostructured high-entropy alloys with multiple principal elements: novel alloy design concepts and outcomes. Adv Eng Mater, 2004, 6: 299-303 CrossRef Google Scholar

[2] Zhang Y, Zuo TT, Tang Z, et al. Microstructures and properties of high-entropy alloys. Prog Mater Sci, 2014, 61: 1-93 CrossRef Google Scholar

[3] Zhang W, Liaw PK, Zhang Y. Science and technology in high-entropy alloys. Sci China Mater, 2018, 61: 2-22 CrossRef Google Scholar

[4] Rost CM, Sachet E, Borman T, et al. Entropy-stabilized oxides. Nat Commun, 2015, 6: 8485 CrossRef PubMed ADS Google Scholar

[5] Bérardan D, Franger S, Meena AK, et al. Room temperature lithium superionic conductivity in high entropy oxides. J Mater Chem A, 2016, 4: 9536-9541 CrossRef Google Scholar

[6] Bérardan D, Franger S, Dragoe D, et al. Colossal dielectric constant in high entropy oxides. Phys Status Solidi RRL, 2016, 10: 328-333 CrossRef ADS arXiv Google Scholar

[7] Rost CM, Rak Z, Brenner DW, et al. Local structure of the MgxNixCoxCuxZnxO (x = 0.2) entropy-stabilized oxide: An EXAFS study. J Am Ceram Soc, 2017, 100: 2732-2738 CrossRef Google Scholar

[8] Meisenheimer PB, Kratofil TJ, Heron JT. Giant enhancement of exchange coupling in entropy-stabilized oxide heterostructures. Sci Rep, 2017, 7: 13344 CrossRef PubMed ADS Google Scholar

[9] Jiang S, Hu T, Gild J, et al. A new class of high-entropy perovskite oxides. Scripta Mater, 2018, 142: 116-120 CrossRef Google Scholar

[10] Sarkar A, Velasco L, Wang D, et al. High entropy oxides for reversible energy storage. Nat Commun, 2018, 9: 3400 CrossRef PubMed ADS Google Scholar

[11] Braun JL, Rost CM, Lim M, et al. Charge-induced disorder controls the thermal conductivity of entropy-stabilized oxides. Adv Mater, 2018, 30: 1805004 CrossRef PubMed Google Scholar

[12] Sarkar A, Djenadic R, Wang D, et al. Rare earth and transition metal based entropy stabilised perovskite type oxides. J Eur Ceramic Soc, 2018, 38: 2318-2327 CrossRef Google Scholar

[13] Anand G, Wynn AP, Handley CM, et al. Phase stability and distortion in high-entropy oxides. Acta Mater, 2018, 146: 119-125 CrossRef Google Scholar

[14] Hong W, Chen F, Shen Q, et al. Microstructural evolution and mechanical properties of (Mg,Co,Ni,Cu,Zn)O high-entropy ceramics. J Am Ceram Soc, 2018, 375: jace.16075 CrossRef Google Scholar

[15] Castle E, Csanádi T, Grasso S, et al. Processing and properties of high-entropy ultra-high temperature carbides. Sci Rep, 2018, 8: 8609 CrossRef PubMed ADS Google Scholar

[16] Sarker P, Harrington T, Toher C, et al. High-entropy high-hardness metal carbides discovered by entropy descriptors. Nat Commun, 2018, 9: 4980 CrossRef PubMed ADS arXiv Google Scholar

[17] Yan X, Constantin L, Lu Y, et al. (Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)C high-entropy ceramics with low thermal conductivity. J Am Ceram Soc, 2018, 101: 4486-4491 CrossRef Google Scholar

[18] Dusza J, Švec P, Girman V, et al. Microstructure of (Hf-Ta-Zr-Nb)C high-entropy carbide at micro and nano/atomic level. J Eur Ceramic Soc, 2018, 38: 4303-4307 CrossRef Google Scholar

[19] Feng L, Fahrenholtz WG, Hilmas GE, et al. Synthesis of single-phase high-entropy carbide powders. Scripta Mater, 2019, 162: 90-93 CrossRef Google Scholar

[20] Harrington TJ, Gild J, Sarker P, et al. Phase stability and mechanical properties of novel high entropy transition metal carbides. Acta Mater, 2019, 166: 271-280 CrossRef Google Scholar

[21] Ye B, Wen T, Huang K, et al. First-principles study, fabrication, and characterization of (Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)C high-entropy ceramic. J Am Ceram Soc, 2019, 102: 4344-4352 CrossRef Google Scholar

[22] Gild J, Zhang Y, Harrington T, et al. High-entropy metal diborides: A new class of high-entropy materials and a new type of ultrahigh temperature ceramics. Sci Rep, 2016, 6: 37946 CrossRef PubMed ADS Google Scholar

[23] Wang YP, Gan GY, Wang W, et al. Ab initio prediction of mechanical and electronic properties of ultrahigh temperature high-entropy ceramics (Hf0.2Zr0.2Ta0.2M0.2Ti0.2)B2 (M = Nb, Mo, Cr). Phys Status Solidi B, 2018, 255: 1800011 CrossRef ADS Google Scholar

[24] Mayrhofer PH, Kirnbauer A, Ertelthaler P, et al. High-entropy ceramic thin films: A case study on transition metal diborides. Scripta Mater, 2018, 149: 93-97 CrossRef Google Scholar

[25] Tallarita G, Licheri R, Garroni S, et al. Novel processing route for the fabrication of bulk high-entropy metal diborides. Scripta Mater, 2019, 158: 100-104 CrossRef Google Scholar

[26] Zhang Y, Guo WM, Jiang ZB, et al. Dense high-entropy boride ceramics with ultra-high hardness. Scripta Mater, 2019, 164: 135-139 CrossRef Google Scholar

[27] Lai CH, Lin SJ, Yeh JW, et al. Preparation and characterization of AlCrTaTiZr multi-element nitride coatings. Surf Coatings Tech, 2006, 201: 3275-3280 CrossRef Google Scholar

[28] Hsieh MH, Tsai MH, Shen WJ, et al. Structure and properties of two Al–Cr–Nb–Si–Ti high-entropy nitride coatings. Surf Coatings Tech, 2013, 221: 118-123 CrossRef Google Scholar

[29] Jin T, Sang X, Unocic RR, et al. Mechanochemical-assisted synthesis of high-entropy metal nitride via a soft urea strategy. Adv Mater, 2018, 30: 1707512 CrossRef PubMed Google Scholar

[30] Qin Y, Liu JX, Li F, et al. A high entropy silicide by reactive spark plasma sintering. J Adv Ceram, 2019, 8: 148-152 CrossRef Google Scholar

[31] Dai FZ, Zhou Y, Sun W. Segregation of solute atoms (Y, Nb, Ta, Mo and W) in ZrB2 grain boundaries and their effects on grain boundary strengths: A first-principles investigation. Acta Mater, 2017, 127: 312-318 CrossRef Google Scholar

[32] Ran S, Van der Biest O, Vleugels J. ZrB2 powders synthesis by borothermal reduction. J Am Ceramic Soc, 2010, CrossRef Google Scholar

[33] Guo WM, Zhang GJ. Reaction processes and characterization of ZrB2 powder prepared by boro/carbothermal reduction of ZrO2 in vacuum. J Am Ceramic Soc, 2009, 92: 264-267 CrossRef Google Scholar

[34] Zhao H, He Y, Jin Z. Preparation of zirconium boride powder. J Am Ceramic Soc, 1995, 78: 2534-2536 CrossRef Google Scholar

[35] Zeng L, Wei W, Sun S, et al. Powder characteristics, sinterability, and mechanical properties of TiB2 prepared by three reduction methods. J Am Ceram Soc, 2019, 102: 4511-4519 CrossRef Google Scholar

[36] You Y, Tan DW, Guo WM, et al. TaB2 powders synthesis by reduction of Ta2O5 with B4C. Ceramics Int, 2017, 43: 897-900 CrossRef Google Scholar

[37] Feng L, Kim JM, Lee SH, et al. Synthesis of a fine (Ta0.8,Hf0.2)C powder from carbide or oxide powder mixtures. J Am Ceram Soc, 2016, 99: 1129-1132 CrossRef Google Scholar

[38] Wang H, Lee SH, Kim HD, et al. Nano-hafnium diboride powders synthesized using a spark plasma sintering apparatus. J Am Ceram Soc, 2012, 95: 1493-1496 CrossRef Google Scholar

[39] Xie J, Fu Z, Wang Y, et al. Synthesis of nanosized zirconium carbide powders by a combinational method of sol–gel and pulse current heating. J Eur Ceramic Soc, 2014, 34: 13.e1-13.e7 CrossRef Google Scholar

[40] Wang R, Wang Y, Fu Z, et al. Spark plasma sintering of transparent YAG ceramics assisted by the YAH–YAG phase transformation. J Eur Ceramic Soc, 2016, 36: 2153-2156 CrossRef Google Scholar

[41] Rietveld HM. Line profiles of neutron powder-diffraction peaks for structure refinement. Acta Cryst, 1967, 22: 151-152 CrossRef Google Scholar

[42] Toby BH. EXPGUI, a graphical user interface for GSAS. J Appl Crystlogr, 2001, 34: 210-213 CrossRef Google Scholar

[43] Evans AG, Charles EA. Fracture toughness determinations by indentation. J Am Ceramic Soc, 1976, 59: 371-372 CrossRef Google Scholar

[44] Avilés MA, Córdoba JM, Sayagués MJ, et al. Mechanosynthesis of Hf1−xZrxB2 solid solution and Hf1−xZrxB2/SiC composite powders. J Am Ceramic Soc, 2010, 93: 696-702 CrossRef Google Scholar

[45] Liu D, Wen T, Ye B, et al. Molten salt synthesis, characterization, and formation mechanism of superfine (HfxZr1−x)B2 solid-solution powders. J Am Ceram Soc, 2019, 102: 3763-3770 CrossRef Google Scholar

[46] Zhou N, Hu T, Huang J, et al. Stabilization of nanocrystalline alloys at high temperatures via utilizing high-entropy grain boundary complexions. Scripta Mater, 2016, 124: 160-163 CrossRef Google Scholar

[47] Lei Z, Liu X, Wang H, et al. Development of advanced materials via entropy engineering. Scripta Mater, 2019, 165: 164-169 CrossRef Google Scholar

[48] Zou J, Zhang GJ, Kan YM, et al. Hot-pressed ZrB2-SiC ceramics with VC addition: chemical reactions, microstructures, and mechanical properties. J Am Ceramic Soc, 2009, 92: 2838-2846 CrossRef Google Scholar

[49] Zhang Y, Jiang ZB, Sun SK, et al. Microstructure and mechanical properties of high-entropy borides derived from boro/carbothermal reduction. J Eur Ceramic Soc, 2019, 39: 3920-3924 CrossRef Google Scholar

[50] Mukhopadhyay A, Raju GB, Basu B, et al. Correlation between phase evolution, mechanical properties and instrumented indentation response of TiB2-based ceramics. J Eur Ceramic Soc, 2009, 29: 505-516 CrossRef Google Scholar

[51] Chamberlain AL, Fahrenholtz WG, Hilmas GE, et al. High-strength zirconium diboride-based ceramics. J Am Ceramic Soc, 2004, 87: 1170-1172 CrossRef Google Scholar

[52] Sairam K, Sonber JK, Murthy TSRC, et al. Reaction spark plasma sintering of niobium diboride. Int J Refractory Met Hard Mater, 2014, 43: 259-262 CrossRef Google Scholar

[53] Ni DW, Zhang GJ, Kan YM, et al. Hot pressed HfB2 and HfB2-20 vol%SiC ceramics based on HfB2 powder synthesized by borothermal reduction of HfO2. Int J Appl Ceramic Tech, 2010, 7: 830-836 CrossRef Google Scholar

[54] Licheri R, Orrù R, Musa C, et al. Synthesis, densification and characterization of TaB2–SiC composites. Ceramics Int, 2010, 36: 937-941 CrossRef Google Scholar

  • Figure 1

    (a) Molar content of the products in equilibrium as a function of the temperature from room temperature (RT) to 2000°C at a partial pressure of 10 Pa. The input amounts of the reactants are based on Reaction (1). (b) The effects of B4C amount on the progress of reactions in MOx-B4C system at 1600°C.

  • Figure 2

    XRD patterns of (a, b) HEB powders synthesized at 1800°C and (c, d) HEB3 powders synthesized at 1300–1800°C.

  • Figure 3

    Back scattered electron (BSE) image of the (a) HEB3-13 and (b) HEB3-16 powders, showing the presence of unreacted oxides, unreacted B4C and newly formed ultra-fine diboride particles as-arrowed. (c, d) Higher magnification images of the ultra-fine diboride particles in (a) and (b). (e) SEM image of the HEB3-18 powders.

  • Figure 4

    HRTEM images of HEB3 powders synthesized at (a) 1300 and (c) 1800°C. The fast Fourier transform images of (a) and (c) were inserted as (b) and (d).

  • Figure 5

    (a) TEM image of the HEB3-13 powders shows an agglomeration of newly formed ultra-fine diborides grains. STEM-mappings of one of the agglomerate regions indicate the quinary solid solution reaction had occurred at 1300°C. (b) TEM image and STEM-mappings of the HEB3-18 powders reveal the unevenly atomic distribution within grains. Note that some circled regions have different concentrations of Nb.

  • Figure 6

    (a) BSE image of the HEB3-13 powders and corresponding EDS-mappings, (b–d) point EDS results showing the presence of (Ti, Ta)-rich regions, (Zr,Hf)-rich regions and unreacted (Zr,Hf)O2. The circled regions in the Nb, Zr and Hf mappings revealing the ZrNb-rich smaller particles are superimposed on the ZrHfNb-rich area.

  • Figure 7

    (a) BSE image and corresponding EDS-mappings of HEB3-16, and (b) Rietveld refinement of the XRD patterns of HEB3-16 using MAUD software (Rwp = 9.29%).

  • Figure 8

    Polished surfaces of HEB3 ceramics sintered at (a) 1900°C, (b) 2000°C, and (c) 2050°C.

  • Figure 9

    XRD patterns of the three ceramics.

  • Figure 10

    WDS-mappings of the specimens sintered at (a) 1900°C, (b) 2000°C, and (c) 2050°C, indicating the uneven elemental distribution at 1900°C while the elemental distributions at 2000 and 2050°C are homogenous.

  • Table 1   Sample designations



    Excess B4C









    0 wt%









    5 wt%









    10 wt%









    13 wt%







    According to Reaction (1); b) according to Reaction (2).

  • Table 2   Oxygen and carbon contents in the selected HEB powders


    Oxygen content (wt%)

    Carbon content (wt%)










  • Table 3   Properties of the high-entropy diboride ceramics


    Sinteringtemperature (°C)

    Relativedensity (%)

    Average grain size (µm)

    E (GPa)

    KIC (MPa m1/2)

    Hardness (GPa)





    6.67 ± 1.20


    2.83 ± 0.15

    25.61 ± 0.83 (HV0.2)

    22.44 ± 0.56 (HV1)

    This work




    41.2 ± 8.1



    26.82 ± 1.77 (HV0.2)

    This work







    17.5 ± 1.2 (HV~1)







    4.06 ± 0.35

    21.7 ± 1.1 (HV0.2)






    497 ± 15

    4.64 ± 0.45

    28.6-32.4 (HV1)







    3.5 ± 0.3

    23 ± 0.9 (HV1)







    4.0 ± 0.6

    20.3 ± 0.6 (HV0.5)a







    3.5 ± 0.5

    18.1 ± 0.9 (HV1)







    5.61 ± 0.17

    25.1 ± 0.5 (HV1)


    HV1 data is not available.