SCIENCE CHINA Information Sciences, Volume 62 , Issue 10 : 202403(2019) https://doi.org/10.1007/s11432-019-9918-4

Printed flexible thin-film transistors based on different types of modified liquid metal with good mobility

More info
  • ReceivedMar 6, 2019
  • AcceptedJun 12, 2019
  • PublishedAug 29, 2019



This work was partially supported by National Natural Science Foundation of China Key Project (Grant No. 91748206), Dean's Research Funding and the Frontier Project of the Chinese Academy of Sciences. Qian LI acknowledges the support by China Postdoctoral Science Foundation (Grant No. 2018M641485). The authors are grateful for the support of Beijing DREAM Ink Technologies Co., Ltd.


Figures S1–S8, Tables S1 and S2.


[1] Myny K. The development of flexible integrated circuits based on thin-film transistors. Nat Electron, 2018, 1: 30-39 CrossRef Google Scholar

[2] Di C A, Liu Y, Yu G. Interface engineering: an effective approach toward high-performance organic field-effect transistors.. Acc Chem Res, 2009, 42: 1573-1583 CrossRef PubMed Google Scholar

[3] Wang H, Wei P, Li Y, et al. Tuning the threshold voltage of carbon nanotube transistors by n-type molecular doping for robust and flexible complementary circuits. Proc Natl Acad Sci U. S. A, 2014, 201320045. Google Scholar

[4] Geier M L, Prabhumirashi P L, McMorrow J J. Subnanowatt Carbon Nanotube Complementary Logic Enabled by Threshold Voltage Control. Nano Lett, 2013, 13: 4810-4814 CrossRef PubMed ADS Google Scholar

[5] Kim B, Jang S, Geier M L. High-Speed, Inkjet-Printed Carbon Nanotube/Zinc Tin Oxide Hybrid Complementary Ring Oscillators. Nano Lett, 2014, 14: 3683-3687 CrossRef PubMed ADS Google Scholar

[6] Ding L, Zhang Z, Liang S. CMOS-based carbon nanotube pass-transistor logic integrated circuits. Nat Commun, 2012, 3: 677 CrossRef PubMed ADS Google Scholar

[7] Gao P, Zou J, Li H. Complementary logic gate arrays based on carbon nanotube network transistors.. Small, 2013, 9: 813-819 CrossRef PubMed Google Scholar

[8] Kang B R, Yu W J, Kim K K. Restorable Type Conversion of Carbon Nanotube Transistor Using Pyrolytically Controlled Antioxidizing Photosynthesis Coenzyme. Adv Funct Mater, 2009, 19: 2553-2559 CrossRef Google Scholar

[9] Kim S M, Jang J H, Kim K K. Reduction-controlled viologen in bisolvent as an environmentally stable n-type dopant for carbon nanotubes.. J Am Chem Soc, 2009, 131: 327-331 CrossRef PubMed Google Scholar

[10] Choi Y, Kan J, Secor E B, et al. Capacitively coupled hybrid ion gel and carbon nanotubethin-film transistors for low voltage flexible logic circuits. Adv Funct Mater, 2018, 28: 1802610. Google Scholar

[11] Hong K, Kim Y H, Kim S H. Aerosol jet printed, sub-2 V complementary circuits constructed from P- and N-type electrolyte gated transistors.. Adv Mater, 2014, 26: 7032-7037 CrossRef PubMed Google Scholar

[12] Ha M, Seo J W T, Prabhumirashi P L. Aerosol jet printed, low voltage, electrolyte gated carbon nanotube ring oscillators with sub-5 μs stage delays.. Nano Lett, 2013, 13: 954-960 CrossRef PubMed ADS Google Scholar

[13] Chen H, Cao Y, Zhang J. Large-scale complementary macroelectronics using hybrid integration of carbon nanotubes and IGZO thin-film transistors. Nat Commun, 2014, 5: 4097 CrossRef PubMed ADS Google Scholar

[14] Honda W, Harada S, Ishida S. High-performance, mechanically flexible, and vertically integrated 3D carbon nanotube and InGaZnO complementary circuits with a temperature sensor.. Adv Mater, 2015, 27: 4674-4680 CrossRef PubMed Google Scholar

[15] Han S J, Tang J, Kumar B. High-speed logic integrated circuits with solution-processed self-assembled carbon nanotubes. Nat Nanotech, 2017, 12: 861-865 CrossRef PubMed ADS Google Scholar

[16] Plevachuk Y, Sklyarchuk V, Yakymovych A. Electrical conductivity and viscosity of liquid Sn-Sb-Cu alloys. J Mater Sci-Mater Electron, 2011, 22: 631-638 CrossRef Google Scholar

[17] Zheng Y, He Z, Gao Y. Direct Desktop Printed-Circuits-on-Paper Flexible Electronics. Sci Rep, 2013, 3: 1786 CrossRef ADS Google Scholar

[18] Liu F, Yu Y, Yi L. Liquid metal as reconnection agent for peripheral nerve injury. Sci Bull, 2016, 61: 939-947 CrossRef Google Scholar

[19] Wang L, Liu J. Compatible hybrid 3D printing of metal and nonmetal inks for direct manufacture of end functional devices. Sci China Technol Sci, 2014, 57: 2089-2095 CrossRef Google Scholar

[20] Guo C, Yu Y, Liu J. Rapidly patterning conductive components on skin substrates as physiological testing devices via liquid metal spraying and pre-designed mask. J Mater Chem B, 2014, 2: 5739-5745 CrossRef Google Scholar

[21] Jeong S H, Hagman A, Hjort K. Liquid alloy printing of microfluidic stretchable electronics.. Lab Chip, 2012, 12: 4657-4664 CrossRef PubMed Google Scholar

[22] Yu Y, Zhang J, Liu J. Biomedical Implementation of Liquid Metal Ink as Drawable ECG Electrode and Skin Circuit. PLoS ONE, 2013, 8: e58771 CrossRef PubMed ADS Google Scholar

[23] Wang Q, Yu Y, Yang J. Fast Fabrication of Flexible Functional Circuits Based on Liquid Metal Dual-Trans Printing.. Adv Mater, 2015, 27: 7109-7116 CrossRef PubMed Google Scholar

[24] Matsuzaki R, Tabayashi K. Highly Stretchable, Global, and Distributed Local Strain Sensing Line Using GaInSn Electrodes for Wearable Electronics. Adv Funct Mater, 2015, 25: 3806-3813 CrossRef Google Scholar

[25] Krupenkin T, Taylor J A. Reverse electrowetting as a new approach to high-power energy harvesting. Nat Commun, 2011, 2: 448 CrossRef PubMed ADS Google Scholar

[26] Zhang Q, Gao Y, Liu J. Atomized spraying of liquid metal droplets on desired substrate surfaces as a generalized way for ubiquitous printed electronics. Appl Phys A, 2014, 116: 1091-1097 CrossRef ADS arXiv Google Scholar

[27] Zhang Q, Zheng Y, Liu J. Direct writing of electronics based on alloy and metal (DREAM) ink: A newly emerging area and its impact on energy, environment and health sciences. Front Energy, 2012, 6: 311-340 CrossRef Google Scholar

[28] Kim J, Ahmed T, Nili H. A Physical Unclonable Function With Redox-Based Nanoionic Resistive Memory. IEEE TransInformForensic Secur, 2018, 13: 437-448 CrossRef Google Scholar

[29] Hu Z, Comeras J M M L, Park H. Physically unclonable cryptographic primitives using self-assembled carbon nanotubes. Nat Nanotech, 2016, 11: 559-565 CrossRef PubMed ADS Google Scholar

[30] Xu F, Zhu Y. Highly conductive and stretchable silver nanowire conductors.. Adv Mater, 2012, 24: 5117-5122 CrossRef PubMed Google Scholar

[31] Kim Y, Zhu J, Yeom B. Stretchable nanoparticle conductors with self-organized conductive pathways. Nature, 2013, 500: 59-63 CrossRef PubMed ADS Google Scholar

[32] Park M, Im J, Shin M. Highly stretchable electric circuits from a composite material of silver nanoparticles and elastomeric fibres. Nat Nanotech, 2012, 7: 803-809 CrossRef PubMed ADS Google Scholar

[33] Matsuhisa N, Kaltenbrunner M, Yokota T. Printable elastic conductors with a high conductivity for electronic textile applications. Nat Commun, 2015, 6: 7461 CrossRef PubMed ADS Google Scholar

[34] Stoyanov H, Kollosche M, Risse S. Soft conductive elastomer materials for stretchable electronics and voltage controlled artificial muscles.. Adv Mater, 2013, 25: 578-583 CrossRef PubMed Google Scholar

[35] Chun K Y, Oh Y, Rho J. Highly conductive, printable and stretchable composite films of carbon nanotubes and silver. Nat Nanotech, 2010, 5: 853-857 CrossRef PubMed ADS Google Scholar

[36] Sekitani T, Nakajima H, Maeda H. Stretchable active-matrix organic light-emitting diode display using printable elastic conductors. Nat Mater, 2009, 8: 494-499 CrossRef PubMed ADS Google Scholar

[37] Gelinck G H, Huitema H E A, van Veenendaal E. Flexible active-matrix displays and shift registers based on solution-processed organic transistors. Nat Mater, 2004, 3: 106-110 CrossRef PubMed ADS Google Scholar

[38] Gamota D R, Brazis P, Kalyanasundaram K, et al. Printed Organic and Molecular Electronics. New York: Springer Science & Business Media, 2013. Google Scholar

[39] Zheng Y, He Z Z, Yang J. Personal electronics printing via tapping mode composite liquid metal ink delivery and adhesion mechanism. Sci Rep, 2015, 4: 4588 CrossRef PubMed ADS Google Scholar

[40] Cao Q, Xia M, Kocabas C. Gate capacitance coupling of singled-walled carbon nanotube thin-film transistors. Appl Phys Lett, 2007, 90: 023516 CrossRef ADS Google Scholar

[41] Ante F, K?lblein D, Zaki T. Contact resistance and megahertz operation of aggressively scaled organic transistors.. Small, 2012, 8: 73-79 CrossRef PubMed Google Scholar

[42] Cao C, Andrews J B, Kumar A. Improving Contact Interfaces in Fully Printed Carbon Nanotube Thin-Film Transistors. ACS Nano, 2016, 10: 5221-5229 CrossRef Google Scholar

[43] Okimoto H, Takenobu T, Yanagi K. Tunable carbon nanotube thin-film transistors produced exclusively via inkjet printing.. Adv Mater, 2010, 22: 3981-3986 CrossRef PubMed Google Scholar

[44] Andrews J B, Mondal K, Neumann T V. Patterned Liquid Metal Contacts for Printed Carbon Nanotube Transistors. ACS Nano, 2018, 12: 5482-5488 CrossRef Google Scholar

[45] Liu C, Xu Y, Li Y. Critical Impact of Gate Dielectric Interfaces on the Contact Resistance of High-Performance Organic Field-Effect Transistors. J Phys Chem C, 2013, 117: 12337-12345 CrossRef Google Scholar

[46] Yu M, Wan H, Cai L. Fully Printed Flexible Dual-Gate Carbon Nanotube Thin-Film Transistors with Tunable Ambipolar Characteristics for Complementary Logic Circuits. ACS Nano, 2018, 12: 11572-11578 CrossRef Google Scholar

[47] Goh R G S, Bell J M, Motta N, et al. p-Channel, n-Channel and ambipolar field-effect transistors based on functionalized carbon nanotube networks. Superlattices Microst, 2009, 46: 347--356. Google Scholar

[48] Allard S, Forster M, Souharce B. Organic semiconductors for solution-processable field-effect transistors (OFETs).. Angew Chem Int Ed, 2008, 47: 4070-4098 CrossRef PubMed Google Scholar

[49] Sirringhaus H. Device Physics of Solution-Processed Organic Field-Effect Transistors. Adv Mater, 2005, 17: 2411-2425 CrossRef Google Scholar

[50] Sun Y, Rogers J A. Inorganic Semiconductors for Flexible Electronics. Adv Mater, 2007, 19: 1897-1916 CrossRef Google Scholar

[51] Yan H, Chen Z, Zheng Y. A high-mobility electron-transporting polymer for printed transistors. Nature, 2009, 457: 679-686 CrossRef PubMed ADS Google Scholar

[52] Chortos A, Lim J, To J W F. Highly stretchable transistors using a microcracked organic semiconductor.. Adv Mater, 2014, 26: 4253-4259 CrossRef PubMed Google Scholar

[53] Kang S J, Kocabas C, Ozel T. High-performance electronics using dense, perfectly aligned arrays of single-walled carbon nanotubes. Nat Nanotech, 2007, 2: 230-236 CrossRef PubMed ADS Google Scholar

[54] Léonard F, Tersoff J. Novel Length Scales in Nanotube Devices. Phys Rev Lett, 1999, 83: 5174-5177 CrossRef ADS Google Scholar

[55] Yang Y, Ding L, Han J. High-Performance Complementary Transistors and Medium-Scale Integrated Circuits Based on Carbon Nanotube Thin Films. ACS Nano, 2017, 11: 4124-4132 CrossRef Google Scholar

[56] Zhao Y, Li Q, Xiao X. Three-Dimensional Flexible Complementary Metal-Oxide-Semiconductor Logic Circuits Based On Two-Layer Stacks of Single-Walled Carbon Nanotube Networks. ACS Nano, 2016, 10: 2193-2202 CrossRef Google Scholar

[57] Geier M L, McMorrow J J, Xu W. Solution-processed carbon nanotube thin-film complementary static random access memory. Nat Nanotech, 2015, 10: 944-948 CrossRef PubMed ADS Google Scholar

[58] Ha T J, Chen K, Chuang S. Highly Uniform and Stable n-Type Carbon Nanotube Transistors by Using Positively Charged Silicon Nitride Thin Films. Nano Lett, 2015, 15: 392-397 CrossRef PubMed ADS Google Scholar

[59] Li G, Li Q, Jin Y. Fabrication of air-stable n-type carbon nanotube thin-film transistors on flexible substrates using bilayer dielectrics. Nanoscale, 2015, 7: 17693-17701 CrossRef PubMed ADS Google Scholar

[60] Ng T N, Daniel J H, Sambandan S. Gate bias stress effects due to polymer gate dielectrics in organic thin-film transistors. J Appl Phys, 2008, 103: 044506 CrossRef ADS Google Scholar

[61] Richards T, Sirringhaus H. Bias-stress induced contact and channel degradation in staggered and coplanar organic field-effect transistors. Appl Phys Lett, 2008, 92: 023512 CrossRef ADS Google Scholar

[62] Salleo A, Street R A. Light-induced bias stress reversal in polyfluorene thin-film transistors. J Appl Phys, 2003, 94: 471-479 CrossRef ADS Google Scholar

  • Figure 1

    (Color online) Flexible liquid metal conductors fabricated by the doping method. (a) SEM images of a liquid metal EGaIn droplet and LM-1: GaSn-Ag@Cu, LM-2: GaIn-Ag@Cu-1, LM-3: GaIn-Ag@Cu-2, LM-4: GaIn-Ag@Cu-3, LM-5: GaIn-Ni-CNTs, LM-6: GaIn-Ni, and LM-7: GaIn-CNTs. Scale bar, 50 $\mu$m. The doping concentration of the different doping elements results in different morphologies. (b) EDS mapping of LM-1. The overlapped mappings of the GaSn-Ag@Cu liquid metal clearly show the distribution of gallium, tin, and copper, and the presence of nanomaterials covering the surface. (c) EDS spectra of the GaSn-Ag@Cu (LM-1), GaIn-Ag@Cu-1 (LM-2), and GaIn-Ag@Cu-2 (LM-3) electrodes by printing. (d) A comparison of this work to recent work on elastic conductors, including Ag nanowires (Ag NW), Au nanoparticles (Au NP), Ag nanoparticles (Ag NP), multi-walled carbon nanotubes (MWCNT), single-walled carbon nanotubes (SWCNT), polyaniline (PANI), and this study (corresponds to red star). Our liquid metals show the best conductivity and stretchability. Inset: plot showing the conductivity of the seven metals.

  • Figure 2

    (Color online) Printed liquid metal CNT transistors on flexible films. (a) Schematic of a flexible LM/CTFT device. (b) and (c) Image of an array of LM/CTFTs on a thin PET. The devices are fabricated with printing processes. (d) A metallographic microscope image of the channel region. Scale bar, 50 $\mu$m.

  • Figure 3

    (Color online) Performance under ambient conditions of representative liquid metal CNT transistors with a CNT semiconductor and various liquid metal electrodes. The TFT transfer plot of the current versus $V_{\rm~GS}$ for (a) LM-1/CNT, (b) LM-2/CNT, and (c) LM-3/CNT devices at $V_{\rm~DS}=|5|$ V. The channel length and width of all devices are 50 $\mu$m and 2000 $\mu$m, respectively. (d) TLM plot of the total resistance ($R_{\rm~total}$) as a function of channel length ($L_{\rm~ch}$) for each type of metal/CNT contact configuration. (e) Plot of the mobilities versus transconductance to compare the representative flexible TFTs reported in the literature. Our TFTs exhibit the highest mobilities.

  • Figure 4

    (Color online) LM/CTFT stability data under ambient conditions. (a) and (b) LM/CTFTs performance, including field-effect mobility and on/off current ratio as a function of the bending cycles. All metrics exhibit negligible variations after 1000 cycles, indicating the excellent flexibility of the devices. (c) and (d) Transistor performance parameters versus time plots for the LM/CTFTs. All metrics exhibit negligible variations after 50 d, indicating the excellent reliability of the devices. The channel length and width for all devices are 50 and 2000 $\mu$m, respectively.

  • Table 1   Different doping elements and mass ratio of seven kinds of liquid metal$^{\rm~a)}$
    Liquid metal Raw materials Mass ratio Mass ratio of elements
    crlr)4-10GaInSnCuNiCOcrGaSn-Ag@CuGaSn, $H_1$(Ag@Cu)100:1574.94%10.20%6.56%7.27%1.03%crGaIn-Ag@Cu-1EGaIn, $H_{20}$(Ag@Cu)100:1566.21%27.50%2.33%3.95%–crGaIn-Ag@Cu-2EGaIn, $H_1$(Ag@Cu)100:1067.86%23.41%2.88%5.85%–crGaIn-Ag@Cu-3EGaIn, $C_1$(Ag@Cu)100:1568.19%22.68%2.13%6.12%0.88%crGaIn-Ni-CNTsEGaIn, Ni, CWNT100:2:1.570.94%21.78%1.05%6.22%–crGaIn-NiEGaIn, Ni100:469.08%23.58%1.12%6.22%–crGaIn-CNTEGaIn, CNT100:272.30%21.21%6.49%–cr