SCIENCE CHINA Materials, Volume 63 , Issue 7 : 1300-1309(2020) https://doi.org/10.1007/s40843-020-1351-3

Micro/nano processing of natural silk fibers with near-field enhanced ultrafast laser

More info
  • ReceivedFeb 29, 2020
  • AcceptedApr 12, 2020
  • PublishedApr 30, 2020


Funded by

We acknowledge the support from the National Key R&D Program of China(2017YFB1104300,2016YFA0200103,2018YFB1107200)

the National Program for the Support of Top-notch Young Professionals

and the National Natural Science Foundation of China(51775303)


We thank Maosheng Chai, Shuang Li, and Dr. Han Li for the help with experimental tests. We thank Dr. Baihui Liang, Dr. Taotao Sun, Dr. Hengqian Hu, and Dr. Chuang Li for the experimental assistance and discussions. We acknowledge the support from the National Key R&D Program of China (2017YFB1104300, 2016YFA0200103 and 2018YFB1107200), the National Program for the Support of Top-notch Young Professionals, and the National Natural Science Foundation of China (51775303).

Interest statement

The authors declare no conflict of interest.

Contributions statement

Qiao M and Wang H contributed equally to this work. Yan J and Zhang Y supervised the project. Qiao M contributed to the nano-processing of silk fibers, mechanism analysis, and simulations. Wang H and Qiao M conducted the characterization of SEM. Wang H contributed to the AFM characterization, Raman measurements, XPS analysis, and microparticle transfer experiment. Lu H performed the mechanical measurements. Li S prepared the degummed silk fibers. Qu L, Jiang L and Lu Y guided the theoretical analysis part. Wang H, Qiao M, Yan J and Zhang Y co-wrote the paper with feedback from all authors.

Author information

Ming Qiao received his master’s degree in mechanical engineering from the University of Chinese Academy of Sciences in 2015. He is currently a PhD candidate at the Department of Mechanical Engineering, Tsinghua University. His research interests focus on femtosecond laser and micro/nano fabrication.

Huimin Wang received his BSc degree in inorganic nonmetallic material engineering from Jilin University in 2016. He is currently a PhD candidate at the Department of Chemistry, Tsinghua University, China. His current research interest focuses on nanocarbon, silk, and their hybrid materials and their applications in flexible electronics.

Jianfeng Yan received his PhD from the Department of Mechanical Engineering, Tsinghua University in 2013. He is currently an associate professor, Department of Mechanical Engineering, Tsinghua University. His research interests are mainly focused on ultrafast laser and micro/nano fabrication.

Yingying Zhang received her PhD degree in physical chemistry from Peking University in 2007. From June 2008 to June 2011, she worked at Los Alamos National Laboratory (USA) as a postdoctoral research associate. Then, she joined Tsinghua University as an associate professor in July of 2011. Her research focuses on the design and controlled preparation of nanocarbon, silk, and their hybrid materials, aiming to develop high-performance flexible electronics and wearable systems.


Supplementary information

Experimental details and supporting data are available in the online version of the paper.


[1] Omenetto FG, Kaplan DL. New opportunities for an ancient material. Science, 2010, 329: 528-531 CrossRef ADS Google Scholar

[2] Yan M, Ma X, Yang Y, et al. Biofabrication strategy for functional fabrics. Nano Lett, 2018, 18: 6017-6021 CrossRef ADS Google Scholar

[3] Jia T, Wang Y, Dou Y, et al. Moisture sensitive smart yarns and textiles from self-balanced silk fiber muscles. Adv Funct Mater, 2019, 29: 1808241 CrossRef Google Scholar

[4] Zhang W, Ye C, Zheng K, et al. Tensan silk-inspired hierarchical fibers for smart textile applications. ACS Nano, 2018, 12: 6968-6977 CrossRef Google Scholar

[5] Huby N, Vié V, Renault A, et al. Native spider silk as a biological optical fiber. Appl Phys Lett, 2013, 102: 123702 CrossRef ADS Google Scholar

[6] Tao H, Kaplan DL, Omenetto FG. Silk materials-a road to sustainable high technology. Adv Mater, 2012, 24: 2824-2837 CrossRef Google Scholar

[7] Mondia JP, Amsden JJ, Lin D, et al. Rapid nanoimprinting of doped silk films for enhanced fluorescent emission. Adv Mater, 2010, 22: 4596-4599 CrossRef Google Scholar

[8] Kim S, Marelli B, Brenckle MA, et al. All-water-based electron-beam lithography using silk as a resist. Nat Nanotech, 2014, 9: 306-310 CrossRef Google Scholar

[9] Sun YL, Li Q, Sun SM, et al. Aqueous multiphoton lithography with multifunctional silk-centred bio-resists. Nat Commun, 2015, 6: 8612 CrossRef ADS Google Scholar

[10] Hwang SW, Tao H, Kim DH, et al. A physically transient form of silicon electronics. Science, 2012, 337: 1640-1644 CrossRef ADS Google Scholar

[11] Capelli R, Amsden JJ, Generali G, et al. Integration of silk protein in organic and light-emitting transistors. Org Electron, 2011, 12: 1146-1151 CrossRef Google Scholar

[12] Tao H, Hwang SW, Marelli B, et al. Silk-based resorbable electronic devices for remotely controlled therapy and in vivo infection abatement. Proc Natl Acad Sci USA, 2014, 111: 17385-17389 CrossRef ADS Google Scholar

[13] Kim T, McCall JG, Jung YH, et al. Injectable, cellular-scale optoelectronics with applications for wireless optogenetics. Science, 2013, 340: 211-216 CrossRef ADS Google Scholar

[14] Barr MC, Rowehl JA, Lunt RR, et al. Direct monolithic integration of organic photovoltaic circuits on unmodified paper. Adv Mater, 2011, 23: 3500-3505 CrossRef Google Scholar

[15] Hübler A, Trnovec B, Zillger T, et al. Printed paper photovoltaic cells. Adv Energy Mater, 2011, 1: 1018-1022 CrossRef Google Scholar

[16] Tang-Schomer MD, Hu X, Hronik-Tupaj M, et al. Film-based implants for supporting neuron-electrode integrated interfaces for the brain. Adv Funct Mater, 2014, 24: 1938-1948 CrossRef Google Scholar

[17] Kim DH, Viventi J, Amsden JJ, et al. Dissolvable films of silk fibroin for ultrathin conformal bio-integrated electronics. Nat Mater, 2010, 9: 511-517 CrossRef ADS Google Scholar

[18] Maximova K, Wang X, Balčytis A, et al. Silk patterns made by direct femtosecond laser writing. Biomicrofluidics, 2016, 10: 054101 CrossRef Google Scholar

[19] Moore A, Koch M, Mueller K, et al. Precise laser ablation processing of black widow spider silk. Appl Phys A, 2003, 77: 353-357 CrossRef Google Scholar

[20] Jiang HB, Zhang YL, Han DD, et al. Bioinspired fabrication of superhydrophobic graphene films by two-beam laser interference. Adv Funct Mater, 2014, 24: 4595-4602 CrossRef Google Scholar

[21] Tirlapur UK, König K. Targeted transfection by femtosecond laser. Nature, 2002, 418: 290-291 CrossRef ADS Google Scholar

[22] Hanczyc P, Samoc M, Norden B. Multiphoton absorption in amyloid protein fibres. Nat Photon, 2013, 7: 969-972 CrossRef ADS Google Scholar

[23] Zhang YL, Chen QD, Xia H, et al. Designable 3D nanofabrication by femtosecond laser direct writing. Nano Today, 2010, 5: 435-448 CrossRef Google Scholar

[24] Sidhu MS, Kumar B, Singh KP. The processing and heterostructuring of silk with light. Nat Mater, 2017, 16: 938-945 CrossRef ADS Google Scholar

[25] Xu BB, Xia H, Niu LG, et al. Flexible nanowiring of metal on nonplanar substrates by femtosecond-laser-induced electroless plating. Small, 2010, 6: 1762-1766 CrossRef Google Scholar

[26] Wang S, Yu Y, Ma D, et al. High performance hybrid supercapacitors on flexible polyimide sheets using femtosecond laser 3D writing. J Laser Appl, 2017, 29: 022203 CrossRef ADS Google Scholar

[27] Tanaka Y, Obara M. Comparison of resonant plasmon polaritons with MIE scattering for laser-induced near-field nanopatterning: Metallic particle vs dielectric particle. Jpn J Appl Phys, 2009, 48: 122002 CrossRef ADS Google Scholar

[28] Miyanishi T, Sakai T, Nedyalkov NN, et al. Femtosecond-laser nanofabrication onto silicon surface with near-field localization generated by plasmon polaritons in gold nanoparticles with oblique irradiation. Appl Phys A, 2009, 96: 843-850 CrossRef ADS Google Scholar

[29] Lee JY, Hong BH, Kim WY, et al. Near-field focusing and magnification through self-assembled nanoscale spherical lenses. Nature, 2009, 460: 498-501 CrossRef ADS Google Scholar

[30] Tanaka Y, Obara G, Zenidaka A, et al. Femtosecond laser near-field nanoablation patterning using MIE resonance high dielectric constant particle with small size parameter. Appl Phys Lett, 2010, 96: 261103 CrossRef ADS Google Scholar

[31] Xu S, Yao C, Liao W, et al. Experimental study on 800 nm femtosecond laser ablation of fused silica in air and vacuum. Nucl Instruments Methods Phys Res Sect B-Beam Interactions Mater Atoms, 2016, 385: 46-50 CrossRef ADS Google Scholar

[32] Balling P, Schou J. Femtosecond-laser ablation dynamics of dielectrics: Basics and applications for thin films. Rep Prog Phys, 2013, 76: 036502 CrossRef ADS Google Scholar

[33] Xiong W, Zhou YS, He XN, et al. Simultaneous additive and subtractive three-dimensional nanofabrication using integrated two-photon polymerization and multiphoton ablation. Light Sci Appl, 2012, 1: e6 CrossRef ADS Google Scholar

[34] Stuart BC, Feit MD, Herman S, et al. Nanosecond-to-femtosecond laser-induced breakdown in dielectrics. Phys Rev B, 1996, 53: 1749-1761 CrossRef ADS Google Scholar

[35] Jiang L, Wang AD, Li B, et al. Electrons dynamics control by shaping femtosecond laser pulses in micro/nanofabrication: Modeling, method, measurement and application. Light Sci Appl, 2018, 7: 17134 CrossRef ADS Google Scholar

[36] Qiao M, Yan J, Gao B. Ablation of TiO2 surface with a double-pulse femtosecond laser. Optics Commun, 2019, 441: 49-54 CrossRef ADS Google Scholar

[37] Gamaly EG, Rode AV, Luther-Davies B, et al. Ablation of solids by femtosecond lasers: Ablation mechanism and ablation thresholds for metals and dielectrics. Phys Plasmas, 2002, 9: 949-957 CrossRef ADS arXiv Google Scholar

[38] Lazare S, Sionkowska A, Zaborowicz M, et al. Bombyx mori silk protein films microprocessing with a nanosecond ultraviolet laser and a femtosecond laser workstation: Theory and experiments. Appl Phys A, 2012, 106: 67-77 CrossRef ADS Google Scholar

[39] Mero M. On the damage behavior of dielectric films when illuminated with multiple femtosecond laser pulses. Opt Eng, 2005, 44: 051107 CrossRef ADS Google Scholar

[40] Moore WH, Krimm S. Vibrational analysis of peptides, poly-peptides, and proteins. II. β-Poly(L-alanine) and β-poly(L-alanylglycine). Biopolymers, 1976, 15: 2465-2483 CrossRef Google Scholar

[41] Rousseau ME, Lefèvre T, Beaulieu L, et al. Study of protein conformation and orientation in silkworm and spider silk fibers using Raman microspectroscopy. Biomacromolecules, 2004, 5: 2247-2257 CrossRef Google Scholar

[42] Krimm S, Banderkar J. Vibrational spectroscopy and conformation of peptides, polypeptides, and proteins. Adv Protein Chem, 1986, 38: 181-364 CrossRef Google Scholar

[43] Krimm S. Vibrational analysis of conformation in peptides, polypeptides, and proteins. Biopolymers, 1983, 22: 217-225 CrossRef Google Scholar

[44] Moore WH, Krimm S. Vibrational analysis of peptides, poly-peptides, and proteins. I. Polyglycine i. Biopolymers, 1976, 15: 2439-2464 CrossRef Google Scholar

[45] Qiu W, Teng W, Cappello J, et al. Wet-spinning of recombinant silk-elastin-like protein polymer fibers with high tensile strength and high deformability. Biomacromolecules, 2009, 10: 602-608 CrossRef Google Scholar

[46] Porter D, Vollrath F. Silk as a biomimetic ideal for structural polymers. Adv Mater, 2009, 21: 487-492 CrossRef Google Scholar

[47] Mannoor MS, Tao H, Clayton JD, et al. Graphene-based wireless bacteria detection on tooth enamel. Nat Commun, 2012, 3: 763 CrossRef ADS Google Scholar

[48] Qin Z, Compton BG, Lewis JA, et al. Structural optimization of 3D-printed synthetic spider webs for high strength. Nat Commun, 2015, 6: 7038 CrossRef ADS Google Scholar

  • Figure 1

    Two different modes for the processing of silk fiber using an ultrafast laser. (a) Schematic of Mode 1 for far-field laser ablation. (b) Schematic of Mode 2 for localized near-field enhancement-assisted ablation. (c) Surface morphology of a silk fiber. (d) A simulation model of the surface wavy structures and corresponding FDTD results of the optical intensity distribution.

  • Figure 2

    Controlled hole drilling on individual silk fiber by femtosecond laser pulses with different pulse energy fluences. (a) Schematic diagram of drilling holes on a silk fiber using a femtosecond laser. (b) SEM images of the holes drilled by 500 femtosecond laser pulses with different energy fluences. (c) The measured and calculated widths of the holes ablated with different pulse energy fluences. (d) Ultraviolet-visible-infrared absorbance and transmittance spectra of silk fibers in the range of 185–1,000 nm. (e) Spatial distribution of laser intensity and corresponding free electron density. (f, g) Calculated optical intensity distributions when the laser was focused on the fiber with holes drilled by 3.84 and 7.33 J cm−2 femtosecond laser pulses, respectively.

  • Figure 3

    Characterization of laser-processed silk fibers. (a) Raman spectra of the silk fibers at different ablation sites and the spectrum of native silk fiber. (b) Survey XPS spectra of silk fabric before and after ablation with a femtosecond laser. The existing of a Si 2p peak in the full XPS survey spectrum is attributed to a silicon wafer used as a substrate. (c) High-resolution XPS C1s spectrum of silk after ablation with a femtosecond laser (top) and the spectrum of native silkworm silk (bottom). (d) Stress-strain curves of degummed silk fibers after processing using femtosecond lasers with fluences of 2.64 and 5.27 J cm−2, along with that of the native silk. The stress was computed by assuming a constant silk diameter. (e) Comparison of the toughness and Young’s modulus of processed silk and native silk. The error bars indicate standard deviations from seven different samples in each case.

  • Figure 4

    Biocompatible carrier and patterning on silk fabric. (a) A silk fiber as a biocompatible carrier after laser processing. Schematic diagram of the transfer of a PS microsphere into the hole on the silk fiber, (i) perforating individual silk fiber using the femtosecond laser, (ii) a PS microsphere at the tip of the probe, and (iii) a PS microsphere in the hole on the silk fiber. (b) Experimental optical images of the transfer of a PS microsphere into the hole on the silk fiber, (i) a hole on silk fiber, (ii) a PS microsphere at the tip of the probe, and (iii) a PS microsphere in the hole on the silk fiber. (c) The logo of Tsinghua University was patterned on to the silk fabric using the femtosecond laser. There is a coin of ten cents on the right of the silk fabric. (d) The optical microscopy image of the logo of Tsinghua University. (e, f) Optical microscopy images at different amplifications corresponding to the square area shown in (d) showing the ablation of the silk after processing with the femtosecond laser.